tempered glass smoothness not good question
- Jun 26, 2017 -
The tempered glass smoothness not good question may divide into 2 kinds:
  
  1st kind, curved tempered glass smoothness not good question.Usually considers its goodness of fit target to this kind of question, when the curved tempered glass end product appears goodness of fit not to be able to achieve when design request, mainly can appear following 3 kind of phenomena: 
  
(1)product glass and the design requests to appear the distortion deviation.This indicated needs to carry on the curved steel the glass not to be correct on table position laying aside, glass curving middle line and table not parallel, if has this kind of situation, the operator needs to readjust the glass in to begin a movie on Taiwan's position, causes the glass curving middle line and the table is at the parallel condition.
(2)product glass and the design curving depth appears differently.This indicated the steel craft parameter hypothesis has the question: In the heating phase, the glass heating temperature is insufficient; When the cooling period, mainly is the wind grid uptake with under gusty area blowing not synchronization, when blowing opens the blowing first, after opens the blowing.If the canyon wind mouth opens the blowing first, after then takes shape the glass curving depth to be able to enlarge, otherwise, on blows the gusty area to open the blowing first, after the formation the glass curving depth can reduce, does not become the arc according to the designed depth.This time the operator may readjust the craft parameter, appropriate readjustment glass curving depth.
(3)product glass profile quality does not conform to the design requirement.
  
  The operator may the appropriate readjustment heating zone curving time and the sharp quenching time, or the curving section driving chain tightens the degree, through solves this kind of problem to the steel craft parameter or the equipment adjustment.
  
2nd kind, even tempered glass smoothness not good question.This kind of question mainly has following 5 kind of situations:
  
(1) glass when heating on the undersurface existence temperature difference creates glass distortion
①The tempered glass pan turns up.This kind of phenomenon is because the glass is heated up after the heating furnace, appears on the glass the superficial temperature to be higher than the undersurface the temperature situation, maintains this kind of temperature condition the glass to enter the coolingroom to cool, in undercooling, when on glass conditions and so on undersurface cooling temperature and wind pressure same, because on the glass the surface temperature is high, after cooling on the superficial contraction quantity is bigger than the undersurface, can appear the glass pan to turn up the distortion phenomenon.
Has this kind of situation, may the heating furnace base temperature enhancement, reduce as far as possible on the glass the undersurface temperature difference.  
②Tempered glass pan downward curving.This kind of phenomenon is because the glass is heated up after the heating furnace, appears the glass undersurface the temperature to be higher than on the superficial temperature situation, maintains this kind of temperature condition the glass to enter the coolingroom to cool, in undercooling, when on glass conditions and so on undersurface cooling temperature and wind pressure same, because the glass undersurface temperature is high, after cooling the undersurface contraction quantity is bigger than on the surface, can appear the glass pan downward bending strain the phenomenon.Has this kind of situation, may heating furnace base temperature drop, reduce as far as possible on the glass the undersurface temperature difference.
(2) glass when heating middle and side the existence temperature difference creates glass distortion

 glass after heating furnace process heating side, if spot temperature is higher than a temperature, then in the undercooling, on the glass the temperature high middle spot contraction quantity, will be bigger than the temperature low side contraction quantity, when the glass is cooled to the room temperature condition, a glass side size could be bigger than the middle spot the size, will form the big compressed stress in glass side, thus will appear the glass pan downward bending strain the phenomenon.
Similarly, glass after heating furnace process heating, if its side temperature is higher than the middle spot the temperature, then in the undercooling, on the glass the temperature high middle spot contraction quantity will be bigger than the temperature low side contraction quantity, when the glass is cooled to the room temperature condition side, the glass middle spot size could be bigger than a size, will form the big tensile stress in glass side, thus will appear the glass pan to turn up the distortion phenomenon.